Lead-free tin strips have good performance and wide application scenarios in daily industry, but it is easy to oxidize too fast in the storage process. This article will summarize the reasons why lead-free tin strips oxidize too fast.

Lead-free tin strips are used in high temperature hand immersion furnace, and the use temperature is about 350-550℃. What is the reason why the lead-free tin strips oxidize quickly? May be the product furnace temperature is too high, the furnace temperature is too high leading to fast oxidation. It may also be that the furnace has many impurities, and the high temperature tin furnace is easy to increase the copper content, and the copper content is increased, destroying the oxidation. The product is not resistant to high temperature, the product is not subject to this high temperature will also lead to rapid oxidation. Solution, adjust the furnace temperature, to the appropriate furnace temperature. Clean the tin stove and put in new tin. Before purchasing the product, ask the manufacturer how many degrees of furnace temperature the product can withstand before placing an order.

Under high temperature conditions, the solder surface can keep silver and bright state for a long time. It is suitable for hot dip welding process, especially for all kinds of connection wire manufacturing, self-soluble enamored wire dipping tin in transformer manufacturing. Less tin slag, not only reduce bad solder joints, save production costs, and save a lot of time to soak tin.

The above is a summary of the reasons why lead-free tin strips oxidize too quickly. If you have more understanding of the oxidation of lead-free tin strips, please contact us.